FEATURES
High Tg,Low CTE,Low DfLow water absorption,Excellent anti-CAFHalogen,antimony and red phosphorus freeMOT 150℃APPLICATIONS
Automotive,Like MDC,MCU,etc.Advanced HDI for AutomotiveGENERAL PROPERTIES
Item | IPC-TM-650 | Test Condition | Typical value | ||
Glass transition temp. |
| DSC | ℃ | 180 | |
TMA | ℃ | 184 | |||
DMA | ℃ | 210 | |||
CTE,Z-axis | 2.4.24 | α1，TMA | ppm/℃ | 33 | |
α2，TMA | ppm/℃ | 194 | |||
50~260℃，TMA | % | 1.8 | |||
Decomposition Temp. | 2.4.24.6 | TGA | ℃ | 385 | |
T288 | 2.4.24.1 | TMA,unclad | min | >60 | |
Thermal stress | 2.4.13.1 | Copper clad | sec | >120 | |
unclad | sec | >180 | |||
Water absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.1 | |
Peel Strength/18μm | 2.4.8 | as received | lb/in | 6.5 | |
after thermal stress | lb/in | 6.5 | |||
Permittivity(RC50%) | 2.5.5.9 | C-24/23/50,1G | / | 4.2 | |
Loss tagent(RC50%) | 2.5.5.9 | C-24/23/50,1G | / | 0.010 | |
Volume resistivity | 2.5.17.1 | C-96/35/90 | MΩ·cm | 4.70*1010 | |
Surface resistivity | 2.5.17.1 | C-96/35/90 | MΩ | 3.54*108 | |
Arc Resistance | 2.5.1 | sec | 130 | ||
Dielectric Breakdown | 2.5.6 | D48/50+D0.5/23 | kV | 60 | |
Flexural strength | Warp | 2.4.4 | as received | MPa | 550 |
Fill | 2.4.4 | as received | MPa | 450 | |
Flame resistance | UL-94 | A&E-24/125 | / | V0 | |
CTI | C-96/20/65 | IEC-60112 | Rating | PLC3 | |
u Specification sheet:IPC-4101/130, for reference only.
u Above typical value is tasted from CCL1.0mm 7628*5,except Dk/Df,the typical value is only for reference，cannot be used as the basis for judgement.